Trademark PE LDVA1925.4F
| Category: | LDPE+EVA , Low Density Polyethylene + EVA |
| Manufacturer: | Trademark Plastics Corporation |
| Trademark: | Trademark PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZfDffC_Trademark-PE-LDVA1925-4F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Trademark PE LDVA1925.4F is a Low Density Polyethylene + EVA product. It can be processed by coextruded film and is available in North America. Applications of Trademark PE LDVA1925.4F include bags/liners, film and food contact applications. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 4.0 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 25.2 | MPa | |
| TD : Break, 38 µm, Blown Film | 21.7 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 350 | % | |
| TD : Break, 38 µm, Blown Film | 510 | % | |
| Dart Drop Impact (38 µm, Blown Film) | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, Blown Film | 190 | g | |
| TD : 38 µm, Blown Film | 260 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.1 µm, Blown Film) | 75 | ASTM D2457 | |
| Haze (38.1 µm, Blown Film) | 4.5 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 166 to 193 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styropor® P 326 C | BASF Corporation | PS (EPS) | Styropor® |
| Moplen S81S | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| INLUBE POMCGF10TF15 | Infinity LTL Engineered Compounds | Acetal (POM) Copolymer | INLUBE |
| Lupoy® 1300-22 | LG Chem Ltd. | PC | Lupoy® |
| Lutene® XL8080NTS | LG Chem Ltd. | PE, Unspecified | Lutene® |