PELPRENE™ S2002FB
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | PELPRENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZeiS49_PELPRENE-S2002FB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PELPRENE™ S2002FB is a Thermoplastic Polyester Elastomer (TPEE) product. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 1.3 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 65% RH) | 0.38 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore A | 98 | JIS K6301 | |
| Shore D | 57 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| -- | 26.9 | MPa | |
| 50% Strain | 16.6 | MPa | |
| Tensile Elongation (Break) | 560 | % | ASTM D638 |
| Flexural Modulus | 230 | MPa | ASTM D790 |
| Compressive Strength (10% Strain) | 15.8 | MPa | ASTM D695 |
| Taber Abrasion Resistance (1000 Cycles) | 12.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 160 | kN/m | ASTM D624 |
| Compression Set | 65 | % | JIS K6301 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Brittleness Temperature | < -65.0 | °C | JIS K6301 |
| Vicat Softening Temperature | 185 | °C | ASTM D1525 |
| Melting Temperature | 210 | °C | DSC |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength | 25 | kV/mm | JIS K2111 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Resilience | 60 | % | JIS K6301 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BP RPP 4010 TU NAT | Buckeye Polymers, Inc. | PP, Unspecified | BP |
| HiFill® PA6/6 GF14 HS L BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Kumsollan® KSE5155 | Shanghai KumhoSunny Plastics Co., Ltd. | TPV | Kumsollan® |
| Iupilon® EGW2010DR 9005 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LUVOCOM® 1100-8721 | Lehmann & Voss & Co. | PESU | LUVOCOM® |