Epocast 1633 A/B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zeeq4e_Epocast-1633-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION: Epocast® 1633-A/B epoxy syntactic is a medium paste, halogen-free self-extinguishing compound designed for potting fasteners in honeycomb structures. The epoxy syntactic is easily extruded through 1/8 in. (3mm) nozzle orifice, but is non-flowing after application. It is easy to handle in isolated repair areas because the syntactic paste is available in dual-barrel cartridges. Epocast® 1633-A/B epoxy syntactic sets quickly at room temperature. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 0.660 | g/cm³ | ASTM D792 |
| -- 2 | 0.680 | g/cm³ | ASTM D792 |
| -- 3 | 0.730 | g/cm³ | ASTM D792 |
| Viscosity | ASTM D2196 | ||
| -- 4 | Soft-paste | ASTM D2196 | |
| -- 5 | Soft-paste | ASTM D2196 | |
| -- 6 | Paste | ASTM D2196 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (120°C) | 5.0 | hr | |
| Tensile Lap Shear - chromic acid etched al/al (25°C) | 9.65 | MPa | ASTM D1002 |
| Weight Gain 7 | ASTM D570 | ||
| Distilled water : 25°C | 2.5 | % | ASTM D570 |
| Mil-M-5606, hydraulic fluid : 25°C | 0.40 | % | ASTM D570 |
| Skydrol 500-A : 25°C | 0.70 | % | ASTM D570 |
| TTS-735, Type III test fluid : 25°C | 0.30 | % | ASTM D570 |
| Work Life - 10 grams (25°C) | 2.0 - 5.0 | min | ASTM D1338 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Modulus | 1860 | MPa | ASTM D695 |
| Compressive Strength (25°C) | 44.8 | MPa | ASTM D695 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 50 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CURE SCHEDULE : Gel at room temperature plus 5 hours at 120°F (49°C) or gel at room temperature plus 2 hours at 150°F (66°C) or 3 days at room temperature. |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Resin |
| 3 . | System |
| 4 . | Resin |
| 5 . | Hardener |
| 6 . | System |
| 7 . | on immersion - 24 hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Butyrate 264A3720013 Clear, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| Trithene® TX 7010 | Petroquimica Triunfo | LDPE | Trithene® |
| WPP TPO TPO-277 P Black | Washington Penn Plastic Co. Inc. | TPO | WPP TPO |
| Fibrolon® P 8540 | FKuR Kunststoff GmbH | PP, Unspecified | Fibrolon® |
| Ferro PP LPP20BN51AL | Ferro Corporation | PP, Unspecified | Ferro PP |