Braskem PP H358-02
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Braskem Europe GmbH |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZeUwgA_Braskem-PP-H358-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Braskem H358-02 Polypropylene Resin is a homopolymer developed for the manufacturing of monolayer or co-extruded BOPP films. Braskem H358-02 Polypropylene Resin offers excellent processability and is formulated with an optimized stabilization package. Braskem H358-02 Polypropylene Resin does not contain any slip, anti-blocking, or anti-static agents. Applications for Braskem H358-02 Polypropylene Resin
Regulatory Information Braskem H358-02 Polypropylene Resin should comply with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.1 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, Injection Molded) | 33.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, Injection Molded) | 13 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 1350 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Film Puncture Energy 1(30 µm) | 2.80 | J | ASTM D5748 |
| Film Puncture Force 2(30 µm) | 61.0 | N | ASTM D5748 |
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 30 µm, Cast Film | 600 | MPa | |
| 1% Secant, TD : 30 µm, Cast Film | 570 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 6.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(0.45 MPa, Unannealed) | 105 | °C | ISO 75-2/B |
| Vicat Softening Temperature 4 | 155 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Cast Film) | 80 | ASTM D2457 | |
| Haze (30.0 µm, Cast Film) | 1.4 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| 2 . | Cast Film |
| 3 . | Injection Molded |
| 4 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP151T | Southern Polymer, Inc. | PP Homopolymer | PRIMALENE |
| PRIMALENE WPP261N | Southern Polymer, Inc. | PP Impact Copolymer | PRIMALENE |
| APEX® 95-A0121B-69 | Teknor Apex Company | PVC, Flexible | APEX® |
| Plaslube® PEEK CF35 TL5 A | Techmer Engineered Solutions | PEEK | Plaslube® |
| Hostacom X M1 T02 357026 | LyondellBasell Industries | PP, Unspecified | Hostacom |