Gravi-Tech™ GRV-NP-110-W-NAT
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Gravi-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZeDVEA_Gravi-Tech-GRV-NP-110-W-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Gravi-Tech™ GRV-NP-110-W-NAT is a Polyamide 12 (Nylon 12) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of Gravi-Tech™ GRV-NP-110-W-NAT include industrial applications, medical/healthcare and sporting goods. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 11.0 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 8270 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 27.2 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.8 | % | ASTM D638 |
| Flexural Modulus | 5520 | MPa | ASTM D790 |
| Flexural Strength | 48.3 | MPa | ASTM D790 |
| Poisson's Ratio | 0.35 | ASTM E132 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 110 | J/m | ASTM D256A |
| Unnotched Izod Impact (23°C, 3.18 mm, Injection Molded) | 370 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 138 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 87.8 | °C | |
| CLTE | ASTM E831 | ||
| Flow : 0 to 32°C | 6.3E-5 | cm/cm/°C | |
| Flow : 60 to 100°C | 1.0E-4 | cm/cm/°C | |
| Transverse : 0 to 32°C | 5.7E-5 | cm/cm/°C | |
| Transverse : 60 to 100°C | 8.4E-5 | cm/cm/°C | |
| Thermal Conductivity 4 | 3.5 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity (3.18 mm) | 10 to 1.0E+3 | ohms | ASTM D257 |
| Volume Resistivity (3.18 mm) | 10 to 1.0E+3 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 260 to 288 | °C | |
| Mold Temperature | 82.2 to 149 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| 4 . | The value listed as thermal conductivity, ASTM C177, was tested in accordance with ASTM E1461. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 199 X 106955 | RTP Company | PP, Unspecified | RTP |
| TPV Elastoprene® N80A-S | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| Acrylloy 10 | Spartech Plastics | Acrylic, Unspecified | Acrylloy |
| EPS Silver® S400R | INEOS Styrenics International SA | PS (EPS) | EPS Silver® |
| INNOPOL® PP CS 2-9120 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |