Hostacom TRC 453N E
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZdegC2_Hostacom-TRC-453N-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom TRC 453N E is a mineral filled high impact, high stiffness polypropylene copolymer. The grade has been specifically designed for moulding large complex parts that require good impact as well as good stiffnessand improved scratch performance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 23 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.70 to 0.90 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | > 70 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | > 80 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 1750 to 2250 | MPa | ISO 178 |
| Flexural Stress (23°C) | > 28.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 2.0 to 10 | kJ/m² | |
| 23°C | 20 to 50 | kJ/m² |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® 351 | Wacker Chemie AG | Silicone | POWERSIL® |
| XANTAR® 24 U | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| MAGNUM™ 1150 EM | Trinseo | ABS | MAGNUM™ |
| Sumikon® X6952 | SBHPP | Phenolic | Sumikon® |
| Dryflex® SE 40A201 | ELASTO | TPE | Dryflex® |