Infino EN-1052
| Category: | PC , Polycarbonate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZdVtCU_Infino-EN-1052.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Non-halogen flame-retardant material with high heat resistance that can be applied to battery charger |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 19 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.20 mm | 0.54 to 0.66 | % | |
| Across Flow : 3.20 mm | 0.56 to 0.69 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 118 | ASTM D785 | |
| R-Scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1900 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 52.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Break 3 | 61.0 | MPa | ASTM D638 |
| Break | 67.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 94 | % | ASTM D638 |
| Break | 110 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2100 | MPa | ASTM D790 |
| -- 6 | 2100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 75.0 | MPa | ASTM D790 |
| -- 8 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 70 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 710 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 65 | J/m | ASTM D256 |
| 23°C 10 | 61 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 135 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 129 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 121 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 123 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ISO 306/B50 |
| -- | 145 | °C | ISO 306/B120 |
| RTI Elec (1.50 mm) | 130 | °C | UL 746 |
| RTI Imp (1.50 mm) | 130 | °C | UL 746 |
| RTI Str (1.50 mm) | 130 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 2.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 260 to 270 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 10 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 10 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-8425DH | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| NEXUS PP CPP50/2 | Nexus Resin Group, LLC. | PP Impact Copolymer | NEXUS PP |
| Delta ATL-2PT20 -UV | Delta Polymers | Acetal (POM) Copolymer | Delta |
| Dugdale PVC Dynamic PVC Nitrile Flexible Compound | Dugdale Plc | PVC, Flexible | Dugdale PVC |
| Karina WHITE PVC COMPOUND 851-10/1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |