Latamid 6 CUVHPX10 G/35
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zd1PWo_Latamid-6-CUVHPX10-G-35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 6 (PA 6). High viscosity. UV stabilised. Heat stabilised. Toughened. Glass fibres. Heat stabilised. UV stabilised. Good elongation properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.70 to 0.95 | % | |
| Flow : 2.00 mm | 0.35 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 9300 | MPa | |
| 60°C | 6100 | MPa | |
| 90°C | 4600 | MPa | |
| 120°C | 3600 | MPa | |
| 150°C | 3200 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 155 | MPa | |
| Yield, 60°C | 105 | MPa | |
| Yield, 90°C | 80.0 | MPa | |
| Yield, 120°C | 65.0 | MPa | |
| Yield, 150°C | 55.0 | MPa | |
| Break, 23°C | 155 | MPa | |
| Break, 60°C | 105 | MPa | |
| Break, 90°C | 80.0 | MPa | |
| Break, 120°C | 65.0 | MPa | |
| Break, 150°C | 55.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 3.0 | % | |
| Yield, 60°C | 5.0 | % | |
| Yield, 90°C | 6.0 | % | |
| Yield, 120°C | 6.0 | % | |
| Yield, 150°C | 6.0 | % | |
| Break, 23°C | 3.0 | % | |
| Break, 60°C | 6.0 | % | |
| Break, 90°C | 6.0 | % | |
| Break, 120°C | 6.0 | % | |
| Break, 150°C | 6.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 6.5 | kJ/m² | |
| 23°C | 9.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 65 | kJ/m² | |
| -20°C | 65 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Notched Izod Impact | ASTM D256A | ||
| -30°C, 3.20 mm | 90 | J/m | |
| -20°C, 3.20 mm | 95 | J/m | |
| 23°C, 3.20 mm | 110 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 100 | °C | |
| Vicat Softening Temperature | 215 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GF 50 TSU | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Exelene® PS 6800 | Montachem International, Inc. | PS (GPPS) | Exelene® PS |
| LIM™ 8040 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | LIM™ |
| Plaslube® PA6/6 GF30 ML5 HS BK | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| TOTAL Polypropylene PPC 4740WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |