TECHNYL® A 218 V30 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZcR2go_TECHNYL-A-218-V30-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 218 V30 Natural is a polyamide 66, reinforced with 30% of glass fibre, heat stabilized, for injection moulding. This product is available in natural color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.80 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.620 | -- | Internal Method |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Fire and Smoke F Index | I2/F3 | -- | NF F16-101 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 7500 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 190 | 135 | MPa | ISO 527-2/1A |
| Tensile Elongation | ||||
| Break | 3.3 | -- | % | ASTM D638 |
| Break | 3.0 | 4.0 | % | ISO 527-2/1A |
| Flexural Modulus | ||||
| -- | 9000 | -- | MPa | ASTM D790 |
| -- | 9000 | 6400 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 290 | -- | MPa | ASTM D790 |
| -- | 280 | 185 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 80 | 88 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| 23°C | 120 | -- | J/m | ASTM D256 |
| 23°C | 10 | 18 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 60 | 65 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 255 | -- | °C | ASTM D648, ISO 75-2/Af |
| Melting Temperature | ||||
| -- | 263 | -- | °C | ISO 11357-3 |
| -- | 260 | -- | °C | ASTM D3418 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 85°C | 2.5E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 85°C | 2.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 6.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 34 | 29 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.70 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.010 | 0.11 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 600 | 600 | V | |
| Solution B | 500 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 5792N-PE | TSRC Corporation | TPE | T-Blend® |
| Multi-Flex® TPE A7606 UV | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| Hyundai EP PA66 LD150 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| LNP™ LUBRICOMP™ WFL34H compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |
| SEQUEL® 1835-AX BLK | LyondellBasell Industries | PP, Unspecified | SEQUEL® |