Sup-tech B9000EX
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Shanghai Suptech Engineering Plastics Co. Ltd. |
| Trademark: | Sup-tech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZcQPBF_Sup-tech-B9000EX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sup-tech B9000EX is a Polyamide 6 (Nylon 6) product. It can be processed by extrusion or injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | DIN 53479 |
| Melt Mass-Flow Rate (MFR) | 1.0 to 4.0 | g/10 min | DIN 53735 |
| Molding Shrinkage | 0.010 to 0.013 | % | DIN 53464 |
| Water Absorption | DIN 53495 | ||
| 23°C, 24 hr | 1.1 | % | |
| Saturation, 23°C | 6.5 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 60.0 | MPa | DIN 53455 |
| Tensile Strain (Break) | 5.0 | % | DIN 53452 |
| Flexural Modulus | 2000 | MPa | DIN 53457 |
| Flexural Stress | 90.0 | MPa | DIN 53457 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | DIN 53461 | ||
| 0.45 MPa, Unannealed | 160 | °C | |
| 1.8 MPa, Unannealed | 60.0 | °C | |
| Melting Temperature | 220 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Electric Strength | 20 | kV/mm | DIN 53481 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 210 to 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene GC30P200-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| VINIKA® CB70KA | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| ExxonMobil™ PP7035E5 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Polifil® PP RMC-20V | The Plastics Group | PP, Unspecified | Polifil® PP |
| Kangxi® FRPC-10GF | Wuxi Kangxi Plastics Technology Co.,Ltd. | PC | Kangxi® |