Spartech Polycom PP5415
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Spartech Polycom |
| Trademark: | Spartech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zbgobi_Spartech-Polycom-PP5415.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% Glass Reinforced Homopolymer Black Polypropylene compound with ultraviolet stabilization offers a superior level of stiffness and heat deflection performance as compared to mineral filled grades. A Spartech Polycom representative can provide further information on this and other Spartech Polycom products. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.998 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 4.5 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 55.2 | MPa | ASTM D638 |
| -- | 62.1 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | ASTM D638 |
| Fracture | 4.0 | % | ASTM D638 |
| Flexural Modulus - Secant | 3030 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 149 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 127 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-5570U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Baytec® EDG-085A | Covestro - PUR | TSU | Baytec® |
| ESENTTIA 40H92-SBC | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |
| OmniLon™ PA6/6 U GMR36 HS | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| Plenco 04485 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |