AKROLOY® PA CF 40 black (3639)
| Category: | Nylon 66+Nylon 6I/6T , Polyamide 66 + PA 6I/6T |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZaxaWd_AKROLOY-PA-CF-40-black-3639-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROLOY® PA CF 40 black (3639) is a 40% carbon fibre reinforced polyamide blend with high tensile strength and good sliding properties as well as reduced moisture absorption Applications are mechanical highly stressed components with high tensile strength and moisture independent properties |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.33 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.50 | % | |
| Flow | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 30000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 260 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 28500 | MPa | ISO 178 |
| Flexural Stress 2 | 380 | MPa | ISO 178 |
| Flexural Strain at Break 3 | 2.0 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content | 40 | % | ISO 1172 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 45 | kJ/m² | |
| 23°C | 55 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 220 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 110 | °C | ISO 75-2/C |
| Melting Temperature 4 | 255 | °C | DIN EN 11357-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trilliant™ HC 5410-0030RS Natural | PolyOne Corporation | HDPE | Trilliant™ HC |
| AMTOPP PL50 | Inteplast Group | PP, Unspecified | AMTOPP |
| LNP™ THERMOCOMP™ RX10408H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Plenco 04304 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |
| Daelim Po1y® XP9100 | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |