Estane® 58215 TPU
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZaenLy_Estane-58215-TPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Type: Estane® 58215 is a 90A aromatic Polyether-Based Thermoplastic Polyurethane (TPU). Features: Excellent physical properties, hydrolysis resistance and improved temperature resistance. Wide processing window for extrusion. Uses: Blown and flat die/cast film extrusion, Injection and blow molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 5 sec) | 87 - 93 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 43.0 | mg | ASTM D3389 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Set (200% Strain) | 20 | % | ASTM D412 |
| Tensile Stress | ASTM D412 | ||
| 100% strain, 0.762mm | 9.00 | MPa | ASTM D412 |
| 300% strain, 0.762mm | 22.9 | MPa | ASTM D412 |
| Tensile Strength (Break, 0.762 mm) | 65.5 | MPa | ASTM D412 |
| Tensile Elongation (Break, 0.762 mm) | 450 | % | ASTM D412 |
| Tear Strength | |||
| 0.762 mm 1 | 105 | kN/m | ASTM D624 |
| Cracking | 29 | kN/m | ASTM D470 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Volume (23°C, 24 hr, in water) | 1.8 | % | ASTM D471 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -40.0 | °C | DSC |
| Melting Temperature | 175 | °C | DSC |
| Kofler Melting Temperature | 170 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze 2 | 23 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 182 | °C | |
| Cylinder Zone 2 Temp. | 188 | °C | |
| Cylinder Zone 3 Temp. | 193 | °C | |
| Cylinder Zone 4 Temp. | 199 | °C | |
| Adapter Temperature | 204 | °C | |
| Melt Temperature | 202 | °C | |
| Die Temperature | 204 | °C |
| Extrusion instructions |
|---|
| Dew Point: -40°CScreen Pack Recommendation: 20/40/80 |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | Pressed between glass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3783 BLK580 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 205 D Z | RTP Company | Nylon 612 | RTP |
| INSTRUC PCPBTGF30IM | Infinity LTL Engineered Compounds | PC+PBT | INSTRUC |
| Karina BEIGE PVC COMPUOND -E 500D08/201 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| NORYL™ FXN4020H resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |