| RX® 643 is a fiberglass reinforced, ammonia-free, phenolic resole compound, with good dimensional stability and good strength at elevated temperatures. Meets ASTM D-5948 Type GPI-10. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 | g/cm³ | ASTM D792 |
| Apparent Density | 0.80 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (Compression Molded) | 0.15 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.050 | % | ASTM D570 |
| Water Absorption - 48 hrs | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale, Compression Molded) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 96.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 13800 | MPa | ASTM D790 |
| Flexural Strength (Compression Molded) | 186 | MPa | ASTM D790 |
| Compressive Strength | 234 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 59 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, Compression Molded | 280 | °C | |
| 1.8 MPa, Annealed, Compression Molded | > 282 | °C | |
| CLTE - Flow | 1.3E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.50 | W/m/K | ASTM C518 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| -- 2 | 14 | kV/mm | |
| -- 3 | 11 | kV/mm | |
| Arc Resistance | 135 | sec | ASTM D495 |
| Note Message | |
|---|---|
| 1 . | Wet, 60 Hz |
| 2 . | Method A (Short-Time) |
| 3 . | Method B (Step-by-Step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ LH50 | Mando Advanced Materials Co., Ltd. | PP Homopolymer | SEPAZ™ |
| WPP PP PPH5TF2-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Yanshan PS 492L | SINOPEC Beijing Yanshan Petrochemical | PS (HIPS) | Yanshan PS |
| Diakon® CMG334V | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Exxelor™ VA 1803 | ExxonMobil Chemical | TP, Unspecified | Exxelor™ |