REPOL® R070EY
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | REPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZYIfHn_REPOL-R070EY.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| REPOL Polypropylene R070EY is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific catalyst system. Repol R070EY is recommended for use in heat seal layer in heat sealable BOPP and Cast Film. R070EY contains slip and antiblock. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 19.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 11 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3 | 650 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 68.0 | °C | ASTM D648 |
| Melting Temperature | 134 | °C | DSC |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® X680 | Vyncolit N.V. | Phenolic | Vyncolit® |
| Jamplast JPHIPSI | Jamplast, Inc. | PS (HIPS) | Jamplast |
| LUVOCOM® 1100-7890 VP | Lehmann & Voss & Co. | PESU | LUVOCOM® |
| LUVOCOM® 1105-7185 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Hifax BC 72 A/1 3001 | LyondellBasell Industries | PP Copolymer | Hifax |