RTP 1005 TFE 15 FR
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZY5vyS_RTP-1005-TFE-15-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.73 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12400 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 103 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 8960 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 155 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 480 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 210 | °C | |
| 1.8 MPa, Unannealed | 238 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.794 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 216 to 254 | °C | |
| Middle Temperature | 227 to 266 | °C | |
| Front Temperature | 221 to 277 | °C | |
| Mold Temperature | 48.9 to 121 | °C | |
| Injection Pressure | 68.9 to 103 | MPa | |
| Back Pressure | 0.172 to 0.517 | MPa | |
| Screw Speed | 60 to 90 | rpm | |
| Clamp Tonnage | 5.5 to 8.3 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Laser+® (B90A) | DAK Americas LLC | PET | Laser+® |
| LEXAN™ VR2920 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| MAJORIS GFR307 - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| POLYCOMPO PP J709UG | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |
| Sylvin 9600-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |