LNP™ THERMOCOMP™ OC006 compound
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZXaYLG_LNP-THERMOCOMP-OC006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP OC006 is a compound based on PPS-Linear resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound OC-1006 Product reorder name: OC006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 23900 | MPa | ASTM D638 |
| Tensile Strength (Break) | 186 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.2 | % | ASTM D638 |
| Flexural Modulus | 21200 | MPa | ASTM D790 |
| Flexural Strength | 283 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 75 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 640 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 108 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Westlake PVDF Film | Westlake Plastics Company | PVDF | Westlake |
| 3M™ Dyneon™ Fluoroplastic THV 221AZ | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroplastic |
| EXCELLOY TK10 | Techno Polymer Co, Ltd. | ABS+PBT | EXCELLOY |
| KOPA® KN173HI4HSBL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Hifax X 4305 HL86 S01261 | LyondellBasell Industries | PP Copolymer | Hifax |