LEMALLOY® C61HL
| Category: | PPE+Nylon 66 , Polyphenylene Ether + Nylon 66 |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | LEMALLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZXQv2N_LEMALLOY-C61HL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEMALLOY® C61HL is a Polyphenylene Ether + Nylon 66 (PPE+Nylon 66) material. It is available in Asia Pacific, Europe, or North America for injection molding. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.10 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 31.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ||||
| Across Flow : 3.20 mm | 1.1 to 1.3 | -- | % | |
| Flow : 3.20 mm | 1.1 to 1.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2500 | 1600 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 66.0 | 51.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 5.3 | 11 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 42 | 73 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2500 | 1700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 104 | 71.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | 45 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 185 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 9.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 5.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | -- | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | |||
| 1.00 mm | 30 | -- | kV/mm | |
| 3.00 mm | 17 | -- | kV/mm | |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.30 | -- | ||
| 1 MHz | 3.20 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 4.0E-3 | -- | ||
| 1 MHz | 9.4E-3 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 240 to 270 | °C | |
| Middle Temperature | 250 to 290 | °C | |
| Front Temperature | 250 to 290 | °C | |
| Nozzle Temperature | 250 to 290 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NB40 NL IX | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| Stat-Tech™ AT-CB2/000 CR | PolyOne Corporation | Acetal (POM) Copolymer | Stat-Tech™ |
| SUMILITE® PL-1125 | Sumitomo Bakelite Co., Ltd. | Phenolic | SUMILITE® |
| BMC 1050 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Jampilen RCXP598 | Jam Polypropylene Company | PP Random Copolymer | Jampilen |