SABIC® PP PCGH19
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZXIZu0_SABIC-PP-PCGH19.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® PP PCGH19 is typically designed for injection molding of healthcare such as caps and closures, 3-part syringes and other thin walled applications. This grade offers a high stifness combined with excellent flow properties. Due to its narrow molecular weight distribution it is very suitable for thin walled, warpage critical applications. SABIC® PP PCGH19 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 19 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 | |
| Shore Hardness (Shore D) | 71 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1850 | MPa | ASTM D638 |
| -- | 1800 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 37.0 | MPa | ASTM D638 |
| Yield | 37.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 9.0 | % | ASTM D638 |
| Yield | 9.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 25 | J/m | ASTM D256A |
| 23°C | 3.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 90.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 65.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 60.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ASTM D1525, ISO 306/A120 5 6 |
| -- | 94.0 | °C | ASTM D1525, ISO 306/B120 6 7 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 GB 10 TFE 13 SI2 | RTP Company | Nylon 66 | RTP |
| RTP 4085 TFE 15 SI 2 | RTP Company | PPA | RTP |
| TRANSMARE® 14CGF20-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Abistir® TR NATURALE | SO.F.TER. SPA | ABS | Abistir® |
| Celanex® 2302 GV1/30 | Celanese Corporation | PBT | Celanex® |