Glass-fiber reinforced polyphthalamide compound especially suitable for plastic and rubber composites VESTAMID HTplus R1035 is a glass-fiber reinforced (50%), heat-stabilized polyphthalamide compound (PPA) especially suitable for the production of rubber and plastic composites. This process is patented by Evonik Degussa GmbH. Parts of VESTAMID HTplus R1035 can be directly bonded to rubber, e. g., HNBR or FPM, without using any adhesives or adhesion promotors. This base resin is especially suitable for manufacturing parts subjected to high temperature. VESTAMID HTplus R1035 is supplied as cylindrical pellets in polyethylene packaging. Drying at 120°C for at least 4 hours before processing is recommended. For information about processing of VESTAMID HTplus R1035, please contact our experts in the department ApplicationsTechnology of the High Performance Polymers Business Line.

Message

Glass-fiber reinforced polyphthalamide compound especially suitable for plastic and rubber composites

VESTAMID HTplus R1035 is a glass-fiber reinforced (50%), heat-stabilized polyphthalamide compound (PPA) especially suitable for the production of rubber and plastic composites. This process is patented by Evonik Degussa GmbH.

Parts of VESTAMID HTplus R1035 can be directly bonded to rubber, e. g., HNBR or FPM, without using any adhesives or adhesion promotors.

This base resin is especially suitable for manufacturing parts subjected to high temperature.

VESTAMID HTplus R1035 is supplied as cylindrical pellets in polyethylene packaging.

Drying at 120°C for at least 4 hours before processing is recommended.

For information about processing of VESTAMID HTplus R1035, please contact our experts in the department ApplicationsTechnology of the High Performance Polymers Business Line.

General Information
Filler / Reinforcement	Glass Fiber, 50% Filler by Weight
Additive	Heat Stabilizer
Features	Bondability Heat Stabilized High Heat Resistance
Uses	Compounding
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Density	1.64	g/cm³	ISO 1183

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	17000	MPa	ISO 527-2
Tensile Stress (Break)	210	MPa	ISO 527-2
Tensile Strain (Break)	2.0	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-40°C, Complete Break	8.0	kJ/m²
23°C, Complete Break	9.0	kJ/m²
Charpy Unnotched Impact Strength			ISO 179/1eU
-40°C, Complete Break	37	kJ/m²
23°C, Complete Break	57	kJ/m²

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature
--	310	°C	ISO 306/A
--	282	°C	ISO 306/B
Melting Temperature	300 to 315	°C	ISO 11357-3

Resin Grade	Manufacturer	Category	Trademark
WPP PP WPP331	Washington Penn Plastic Co. Inc.	PP Impact Copolymer	WPP PP
Yanshan PS 688B	SINOPEC Beijing Yanshan Petrochemical	PS (GPPS)	Yanshan PS
BCC Resins BC 4558	BCC Products Inc.	Polyester, TS	BCC Resins
Ferro PP LPP25BK87GY	Ferro Corporation	PP, Unspecified	Ferro PP
Lotryl® 20MA08	Arkema	EMA	Lotryl®