Medalist® MD-220
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Medalist® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZVM01d_Medalist-MD-220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This compound is designed for medical and healthcare applications requiring oil resistance. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 2.3 | % | ASTM D955 |
| Transverse flow | 2.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 55 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 2.34 | MPa | ASTM D412 |
| 200% strain | 3.34 | MPa | ASTM D412 |
| Tensile Strength (Break) | 4.00 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 250 | % | ASTM D412 |
| Tear Strength | 13.1 | kN/m | ASTM D624 |
| Compression Set (23°C, 22 hr) | 22 | % | ASTM D395 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 138 - 160 | °C | |
| Middle Temperature | 160 - 182 | °C | |
| Front Temperature | 171 - 193 | °C | |
| Nozzle Temperature | 193 - 216 | °C | |
| Processing (Melt) Temp | 193 - 216 | °C | |
| Mold Temperature | 21.1 - 37.8 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 138 - 149 | °C | |
| Cylinder Zone 2 Temp. | 149 - 160 | °C | |
| Cylinder Zone 3 Temp. | 160 - 182 | °C | |
| Cylinder Zone 5 Temp. | 171 - 193 | °C | |
| Die Temperature | 182 - 204 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoprene® AK6/D NAT003 | SO.F.TER. SPA | PP Homopolymer | Tecnoprene® |
| LCA® PBT 420 Type | UniPlas, Inc. | PBT | LCA® |
| Iupilon® MB2210R | Mitsubishi Engineering-Plastics Corp | PC+ABS | Iupilon® |
| PLEXIGLAS® Sheet Soundstop NT CC | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |
| Sylvin 6224-85 Clear 8411 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |