Order Products : sales@su-jiao.com
Ultramid® Structure A3WG12 LFX BK23215
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZUE4EU_UltramidStructureA3WG12LFXBK23215.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid Structure A3WG12 LFX BK23215 is a 60% long glass-fiber reinforced and heat aging resistant injection molding grade designed for applications requiring excellent strength and stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.70 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.70 | -- | % | ISO 294-4 |
| Flow | 0.40 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 19300 | 15500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 255 | 195 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.8 | 2.1 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 19400 | 15400 | MPa | ISO 178 |
| Flexural Stress (23°C) | 420 | 320 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 40 | 38 | kJ/m² | ISO 179 |
| 23°C | 40 | 35 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 90 | 90 | kJ/m² | ISO 179 |
| 23°C | 90 | 90 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Processing (Melt) Temp | 290 - 310 | °C | |
| Mold Temperature | 80 - 100 | °C | |
| Injection Pressure | 3.50 - 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| LNP™ STAT-KON™ RE0069S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |
| LNP™ LUBRICOMP™ ECL36 compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |
| Lucofin® 1454 | Lucobit AG | Polyolefin, Unspecified | Lucofin® |
| POLYfill PP HIP8040 VT2 | Polykemi AB | PP, Unspecified | POLYfill |
| Adflex Q 108 F | LyondellBasell Industries | TPO (POE) | Adflex |