DuraSurf™ ETA
| Category: | UHMWPE , Ultra High Molecular Weight Polyethylene |
| Manufacturer: | Crown Plastics |
| Trademark: | DuraSurf™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZU6s3G_DuraSurf-ETA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Crown Plastics standard line of Easy-To-Apply wear strips and adhesive backed tapes. Each tape product offers excellent abrasion resistance, low coefficient of friction, high impact strength and high performance properties people have come to expect from UHMW. By providing this exceptional material with an adhesive backing, installation time and costs are significantly reduced. No need for bolts or fasteners, no need to countersink. As a matter of fact, DuraSurf™ ETA also reduces scrap by 75%. When a standard 1/4" thick sheet of UHMW is installed using the traditional mechanical fastening method, 3/16" of the material is lost to the bolt head. This leaves only a 1/16" usable wear surface. You can achieve the same result with a 1/16" DuraSurf™ ETA tape product and eliminate 80% of the time and cost associated with traditional installation methods. Crown Plastics offers a wide range of both rubber and acrylic based adhesive systems to meet virtually any application requirement. AVAILABLE THICKNESS .005" (.125 mm), .010" (.25 mm), .015"(.38 mm), .020" (.5 mm), .031" (.75 mm), .040" (1 mm), .050" (1.3 mm), .062" (1.57 mm), .080" (2 mm) .093" (2.35 mm), 100" (2.5 mm), .125" (3.17 mm) AVAILABLE WIDTHS All dimensions between 1/4" (6.35 mm) and 24" (610 mm) UHMW PROPERTIES
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.930 | g/cm³ | ASTM D792 |
| Crystallinity | ASTM D3417 | ||
| 762.0 µm | 48 | % | |
| 1.52 mm | 47 | % | |
| 3.18 mm | 50 | % | |
| Relative Viscosity | ASTM D4020 | ||
| 762.0 µm | 230 to 350 | cm³/g | |
| 1.52 mm | 230 to 350 | cm³/g | |
| 3.18 mm | 230 to 350 | cm³/g |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay | |||
| 762.0 µm | < 10 | msec | |
| 1.52 mm | < 10 | msec | |
| 3.18 mm | < 10 | msec |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 0.762 mm | 65 | ||
| Shore D, 1.52 mm | 65 | ||
| Shore D, 3.18 mm | 65 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | ||
| 0.762 mm | 725 | MPa | |
| 1.52 mm | 731 | MPa | |
| 3.18 mm | 672 | MPa | |
| Tensile Strength | ASTM D638 | ||
| Yield, 0.762 mm | 23.0 | MPa | |
| Yield, 1.52 mm | 20.0 | MPa | |
| Yield, 3.18 mm | 22.0 | MPa | |
| Break, 0.762 mm | 53.0 | MPa | |
| Break, 1.52 mm | 49.0 | MPa | |
| Break, 3.18 mm | 44.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break, 0.762 mm | 60 | % | |
| Break, 1.52 mm | 460 | % | |
| Break, 3.18 mm | 470 | % | |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic 2 | 0.14 | ||
| vs. Itself - Dynamic 3 | 0.14 | ||
| vs. Itself - Dynamic 4 | 0.13 | ||
| vs. Itself - Static 5 | 0.16 | ||
| vs. Itself - Static 6 | 0.16 | ||
| vs. Itself - Static 7 | 0.16 | ||
| vs. Steel - Dynamic 8 | 0.050 to 0.080 | ||
| vs. Steel - Dynamic 9 | 0.050 to 0.10 | ||
| vs. Steel - Dynamic 10 | 0.10 to 0.22 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 11(3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | |||
| -- 12 | 134 | °C | |
| -- 13 | 136 | °C | |
| CLTE - Flow | ASTM D696 | ||
| -100 to -20°C, 3.18 mm | 9.2E-4 | cm/cm/°C | |
| 20 to 100°C, 3.18 mm | 1.5E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | ||
| 0.762 mm | 1.0E+3 | ohms | |
| 1.52 mm | 1.0E+3 | ohms | |
| 3.18 mm | 1.0E+3 | ohms | |
| Volume Resistivity | ASTM D257 | ||
| 0.762 mm | 6.0E+7 | ohms·cm | |
| 1.52 mm | 1.5E+7 | ohms·cm | |
| 3.18 mm | > 2.0E+7 | ohms·cm | |
| Dielectric Strength (3.18 mm) | 14 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 0.762 mm | 2.39 | ||
| 1.52 mm | 2.29 | ||
| 3.18 mm | 2.28 | ||
| Dissipation Factor | ASTM D150 | ||
| 0.762 mm, 10 kHz | -1.0E-3 | ||
| 0.762 mm, 5 MHz | -1.0E-3 | ||
| 1.52 mm, 10 kHz | -2.0E-3 | ||
| 1.52 mm, 5 MHz | -1.0E-3 | ||
| 3.18 mm, 10 kHz | 0.0 | ||
| 3.18 mm, 5 MHz | 1.0E-3 |
| Note Message | |
|---|---|
| 1 . | 0.125 inches |
| 2 . | 0.03 inches |
| 3 . | 0.125 inches |
| 4 . | 0.06 inches |
| 5 . | 0.03 inches |
| 6 . | 0.06 inches |
| 7 . | 0.125 inches |
| 8 . | Oil |
| 9 . | Water |
| 10 . | Dry |
| 11 . | 5.0 mm Notch Depth |
| 12 . | 0.125 inches |
| 13 . | 0.03 inches |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VDC 200-60 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PVDC | TEKNIFLEX® |
| NYLOY® UB-0010N G50N4N | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| Chemical Resources SAN2500 | Chemical Resources, Inc. | SAN | Chemical Resources |
| Fiberfil® J-60/10 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Sylvin 5132-86 Clear Yellow 4174 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |