Bayflex® XGT-4
| Category: | PUR-Ether/MDI , Polyurethane (Polyether, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Bayflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZTlZAN_Bayflex-XGT-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bayflex XGT 4 is an elastomeric polyurethane system used in the reaction injection molding (RIM) process. The system is supplied as two liquid components: Component A is a modified diphenylmethane diisocyanate (MDI), and Component B is a polyether polyol system. Note: The polyol component phase-separates upon standing and must be thoroughly mixed via mechanical means prior to use. The extended gel time of Bayflex XGT 4 gives equipment designers the flexibility to create large, complex parts that can be molded on existing injection machinery. The resin's excellent surface quality and high impact resistance make it a candidate for agricultural equipment, heavy-duty trucks, specialty transportation, and marine applications. As with any product, use of Bayflex XGT 4 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.04 | g/cm³ | |
| -- 2 | 1.07 | g/cm³ | |
| -- 3 | 1.21 | g/cm³ | |
| Molding Shrinkage - Flow | 1.4 | % | |
| Moisture Content | wt% | ||
| Viscosity | |||
| 25°C 4 | 700 | mPa·s | |
| 25°C 5 | 600 | mPa·s |
| Flammability | Nominal Value | Unit | |
|---|---|---|---|
| Flash Point | |||
| -- 6 | 114 | °C | |
| -- 7 | 213 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| NCO 8 | 23 | % |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (Break) | 13.0 | MPa | |
| Tensile Elongation (Break) | 370 | % | |
| Flexural Modulus | |||
| -30°C | 224 | MPa | |
| 23°C | 25.7 | MPa | |
| 70°C | 14.0 | MPa |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tear Strength | 50.8 | kN/m |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 1.1E-4 | cm/cm/°C |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 65 | ||
| Component B | Mixing ratio by weight: 100 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 60.0 - 70.0 | °C |
| Injection instructions |
|---|
| Chemical Temperature: 32 to 38°CPolyol Nucleation Specific Gravity: 0.75 to 0.80Maximum Shot Time: 8 to 10 secTypical Cure Time, 0.125 in: 2 to 3 min |
| Note Message | |
|---|---|
| 1 . | Component B (Polyol) |
| 2 . | System |
| 3 . | Component A (Isocyanate) |
| 4 . | Component A (Isocyanate) |
| 5 . | Component B (Polyol) |
| 6 . | Component B (Polyol), PMCC |
| 7 . | Component A (Isocyanate), PMCC |
| 8 . | Component A (Isocyanate) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXALEN™ PPH319FX21 | SAX Polymers | PP Homopolymer | SAXALEN™ |
| Gallonprene® GP520-7504 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| EL-Lene™ H5840B | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
| LITEN BB 38 | UNIPETROL RPA | PE Copolymer | LITEN |
| Sylvin 8270-82FU White 1227 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |