LNP™ THERMOCOMP™ 9X02540 compound
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZSV9Gw_LNP-THERMOCOMP-9X02540-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP PDX-02540 is a compound based on a PET+PC Blend containing Proprietary Filler(s). Added feature of this grade is: Flame Retardant. Also known as: LNP* THERMOCOMP* Compound PDX-02540 Product reorder name: 9X02540 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | -9.0E-3 to -7.0E-3 | % | |
| Across Flow : 24 hr | 0.30 to 0.50 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.14 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7660 | MPa | ASTM D638 |
| -- | 7240 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 108 | MPa | ASTM D638 |
| Yield | 103 | MPa | ISO 527-2/5 |
| Break 3 | 108 | MPa | ASTM D638 |
| Break | 103 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.2 | % | ASTM D638 |
| Yield | 2.2 | % | ISO 527-2/5 |
| Break 5 | 2.2 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 7030 | MPa | ASTM D790 |
| -- 7 | 6540 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 149 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 149 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 153 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 51 | J/m | ASTM D256 |
| 23°C 10 | 6.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 560 | J/m | ASTM D4812 |
| 23°C 11 | 39 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 13.6 | J | ASTM D3763 |
| -- | 1.40 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 130 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 133 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 122 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 120 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPH3GF3-UV Black | Washington Penn Plastic Co. Inc. | PP, Unspecified | WPP PP |
| BP Flex 7000 VPL BLK | Buckeye Polymers, Inc. | TPV | BP Flex |
| ExxonMobil™ PP7555KNE2 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Extir® GEO 3000 AE | Versalis S.p.A. | PS (EPS) | Extir® |
| Durethan® B 40 FAM 000000 | LANXESS Corporation | Nylon 6 | Durethan® |