UBESTA XPA 9044 X2
| Category: | Nylon 12 Elast , Polyamide 12 Elastomer |
| Manufacturer: | UBE Engineering Plastics, S.A. |
| Trademark: | UBESTA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZST4HT_UBESTA-XPA-9044-X2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UBESTA XPA 9044 X2 is a thermoplastic polyamide elastomer offering enhanced material properties and good process-ability in injection moulding and extrusion application. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.80 | % | ISO 294-4 |
| Flow direction | 0.20 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 2.5 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 22 | ISO 2039-2 | |
| Durometer Hardness (Shore D) | 44 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 8.00 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 44 | % | ISO 527-2 |
| Fracture | 400 | % | ISO 527-2 |
| Flexural Modulus | 80.0 | MPa | ISO 178 |
| Flexural Stress | 5.00 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 16 | kJ/m² | ISO 179/1eA |
| 23°C | 32 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 51.0 | °C | ISO 75-2/B |
| Melting Temperature (DSC) | 150 | °C | ISO 3146 |
| CLTE - Flow | 2.3E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+10 | ohms·cm | IEC 60093 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.Tensile Strain at Break, ISO 527: >400%Abrasion Loss, ISO 9352, CS-17, 1000 rev.: 9 mg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mar-Bal MB2000-15 | Mar-Bal, Inc. | Polyester, TP | Mar-Bal |
| Sylvin 2907-85C Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ESTAPROP 1040 V2 H | Cossa Polimeri S.r.l. | PP Homopolymer | ESTAPROP |
| DENISTAT A 00U 05 | Vamp Tech | PP Copolymer | DENISTAT |
| Lupox® LW5300M | LG Chem Ltd. | PC+PBT | Lupox® |