LNP™ LUBRICOMP™ JFL34 compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZS6xBQ_LNP-LUBRICOMP-JFL34-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP JFL34 is a compound based on Polyethersulfone resin containing 20% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound JFL-4034 Product reorder name: JFL34 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.61 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 0.50 to 0.70 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.35 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.52 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7080 | MPa | ASTM D638 |
| -- | 7040 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 104 | MPa | ASTM D638 |
| Yield | 103 | MPa | ISO 527-2/5 |
| Break 3 | 97.0 | MPa | ASTM D638 |
| Break | 94.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.5 | % | ASTM D638 |
| Yield | 2.5 | % | ISO 527-2/5 |
| Break 5 | 2.5 | % | ASTM D638 |
| Break | 2.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 6020 | MPa | ASTM D790 |
| -- 7 | 6300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 147 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 147 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 146 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.46 | ||
| vs. Itself - Static | 0.63 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 7.95 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 58.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 73 | J/m | ASTM D256 |
| 23°C 10 | 7.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 540 | J/m | ASTM D4812 |
| 23°C 11 | 33 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 14.1 | J | ASTM D3763 |
| -- | 3.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 219 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 220 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 212 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 212 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.2E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.1E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 360 to 371 | °C | |
| Front Temperature | 371 to 382 | °C | |
| Processing (Melt) Temp | 354 to 371 | °C | |
| Mold Temperature | 138 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Microthene® F FE53200 | LyondellBasell Industries | EVA | Microthene® F |
| Sylvin 8739-70FU Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Carboprene® 1040AVD GRIGIO160 | SO.F.TER. SPA | PP Homopolymer | Carboprene® |
| ICORENE® PP CO14RM | ICO Polymers SA, A Division of A. Schulman | PP Copolymer | ICORENE® |
| Plaskon MUF-2C | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |