EMERGE™ PC 8230-20
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZQ1Wdf_EMERGE-PC-8230-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ 8230-20 advanced resin is an opaque, ignition resistant PC resin that contains no chlorinated or brominated or phosphorous based additives. This resin combines good mechanical and high heat properties and maintains excellent processability and contains mold release agent. EMERGE 8230-20 has a UL 94 V-0 rating at 1.5mm and is UV stabilized. Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.00 mm, Injection Molded) | 2400 | MPa | ISO 527-2/50 |
| Tensile Stress | |||
| Yield, 4.00 mm, Injection Molded | 60.0 | MPa | ISO 527-2 |
| Break, 4.00 mm, Injection Molded | 58.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 4.00 mm, Injection Molded) | 100 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 12 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 3.20 mm, Injection Molded 1 | 750 | J/m | ISO 180 |
| 23°C, Injection Molded | 11 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 125 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 2(1.50 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index 3 | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| 3.00 mm | 960 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 87.0 to 91.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 300 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Method 4A |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 9708 | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| Purell PE 1810 E | LyondellBasell Industries | LDPE | Purell |
| TAROPRENE® 2 A80 E1G | Taro Plast S.p.A. | TPV | TAROPRENE® |
| HiFill® PA11 | Techmer Engineered Solutions | Nylon 11 | HiFill® |
| Braskem PP TI8300C | Braskem America Inc. | PP Impact Copolymer | Braskem PP |