Latigloss 57 G/50 F2
| Category: | PPA , Polyphthalamide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latigloss |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZOpLHg_Latigloss-57-G-50-F2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product with high mechanical properties and exceptional surface finish based on Semi-aromatic polyammide (PPA). Glass fibres. Potentially suitable for food/medical contact application. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.63 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.30 to 0.50 | % | |
| Flow : 2.00 mm | 0.15 to 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 180000 | MPa | |
| 60°C | 15500 | MPa | |
| 90°C | 14000 | MPa | |
| 120°C | 11000 | MPa | |
| 150°C | 5500 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 240 | MPa | |
| Break, 60°C | 225 | MPa | |
| Break, 90°C | 190 | MPa | |
| Break, 120°C | 130 | MPa | |
| Break, 150°C | 70.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 1.8 | % | |
| Break, 60°C | 2.0 | % | |
| Break, 90°C | 2.1 | % | |
| Break, 120°C | 3.5 | % | |
| Break, 150°C | 6.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 285 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 260 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 150 | °C | |
| Vicat Softening Temperature | 260 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 3.0E-6 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 310 to 340 | °C | |
| Mold Temperature | 150 to 170 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1205 T-70A | RTP Company | TPU-Polyether | RTP |
| Quadrathane™ ALC-75A | Biomerics, LLC | TPU-PC | Quadrathane™ |
| TOTAL Polyethylene LDPE 1700 MN 18 C | TOTAL Refining & Chemicals | LDPE | TOTAL Polyethylene |
| Zythane® 6085A | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| LEXAN™ 221R resin | SABIC Innovative Plastics | PC | LEXAN™ |