Ultramid® B3G10 SI
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZO2NLW_Ultramid-B3G10-SI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fibre-reinforced injection moulding grade, with excellent surface quality especially suitable for the production of visible parts with very high stiffness. Optimum surface quality is generally obtained at a very high injection speed. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.57 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 12.0 | -- | cm³/10min | ISO 1133 |
| Viscosity Number (96% H2SO4) | 135 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16500 | 10800 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 235 | 160 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 13500 | 9500 | MPa | ISO 178 |
| Flexural Stress | 340 | 230 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 16 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 20 | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 85 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 95 | 100 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | -- | °C | ISO 75-2/A |
| Additional Information | Dry | Conditioned | ||
|---|---|---|---|---|
| Polymer Abbreviation | PA6-GF50 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec | ||
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 280 | °C | |
| Front Temperature | 290 | °C | |
| Nozzle Temperature | 290 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Injection instructions |
|---|
| Residence Time : <10 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P885 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Alcryn® 4660 BK | Advanced Polymer Alloys | MPR | Alcryn® |
| Boltaron 3030 TruPrint | Boltaron Performance Products | PVC, Rigid | Boltaron |
| Ferro PP TPP20AN85NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| KANEKA H536 | Kaneka North America LLC | CPVC | KANEKA |