Estane® 58219 TPU
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZMytg6_Estane-58219-TPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Type: Estane® 58219 is a 92A aromatic Polyether-Based Thermoplastic Polyurethane (TPU). Features: Excellent physical properties, hydrolysis resistance, low temperature performance and clarity. Wide processing window for extrusion. Uses: Blown and flat die/cast film extrusion, Injection and blow molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 5 sec) | 89 - 95 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 40.0 | mg | ASTM D3389 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Set (200% Strain) | 16 | % | ASTM D412 |
| Tensile Stress | ASTM D412 | ||
| 100% strain, 0.762mm | 9.00 | MPa | ASTM D412 |
| 300% strain, 0.762mm | 22.9 | MPa | ASTM D412 |
| Tensile Strength (Break, 0.762 mm) | 62.1 | MPa | ASTM D412 |
| Tensile Elongation (Break, 0.762 mm) | 470 | % | ASTM D412 |
| Tear Strength | |||
| 0.762 mm 1 | 105 | kN/m | ASTM D624 |
| Cracking | 29 | kN/m | ASTM D470 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Volume (23°C, 24 hr, in water) | 0.50 | % | ASTM D471 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -45.0 | °C | DSC |
| Melting Temperature | 140 | °C | DSC |
| Kofler Melting Temperature | 170 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze 2 | 2.3 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 177 | °C | |
| Cylinder Zone 2 Temp. | 182 | °C | |
| Cylinder Zone 3 Temp. | 188 | °C | |
| Cylinder Zone 4 Temp. | 193 | °C | |
| Adapter Temperature | 199 | °C | |
| Melt Temperature | 196 | °C | |
| Die Temperature | 199 | °C |
| Extrusion instructions |
|---|
| Dew Point: -40°CScreen Pack Recommendation: 20/40/80 |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | Pressed between glass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rigidex® P 451-HP40 | INEOS Olefins & Polymers Europe | PP Copolymer | Rigidex® P |
| RheTech Thermoplastic Polyolefin FT3080-50 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Sylvin 5175-92 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SUPRAN® PA1350 | SAMBARK | Nylon, Unspecified | SUPRAN® |
| IDI SMC S31 (Glass Content 26%) | IDI Composites International | TS, Unspecified | IDI SMC |