EVAL™ FP104B
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | EVAL Europe nv |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZMmt5M_EVAL-FP104B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EVAL™ FP104B is an Ethylene Vinyl Alcohol (EVOH) product. It is available in Europe. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 4.4 | g/10 min | |
| 210°C/2.16 kg | 10 | g/10 min | |
| 230°C/2.16 kg | 18 | g/10 min | |
| Ethylene Content | 32.0 | mol% | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 93 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 11 | % | ISO 527-2 |
| Flexural Modulus | 4800 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability 1 | ISO 14663-2 | ||
| 20°C, 0% RH | 4.0E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 100% RH | 0.38 | cm³·mm/m²/atm/24 hr | |
| 20°C, 35% RH | 6.0E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 65% RH | 8.0E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 85% RH | 0.030 | cm³·mm/m²/atm/24 hr | |
| 20°C, 90% RH | 0.060 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate 2 | 1.6 | g·mm/m²/atm/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -- | 2.0 | kJ/m² | |
| -40°C | 2.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 58.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 178 | °C | ISO 306 |
| Melting Temperature | 183 | °C | ISO 11357-3 |
| Peak Crystallization Temperature | 156 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Annex C |
| 2 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ MH-82 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| SUMIKASUPER® LCP E4006L | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| VENYL VN007 - 8139 | AD majoris | Nylon 66/6 | VENYL |
| TIPPLEN® H 659 F | MOL Petrochemicals Co. Ltd. | PP Homopolymer | TIPPLEN® |
| Generic PBT+PET - Mineral | Generic | PBT+PET | Generic |