ACCUTECH™ SAN930G20L
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZMZy2u_ACCUTECH-SAN930G20L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™ SAN930G20L is a Styrene Acrylonitrile (SAN) product filled with 20% glass fiber. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5000 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 91.0 | MPa | |
| Break | 91.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | |
| Break | 4.0 | % | |
| Flexural Modulus | 7200 | MPa | ASTM D790 |
| Flexural Strength | 123 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 44 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 112 | °C | |
| 1.8 MPa, Unannealed | 98.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800 B-65A Z | RTP Company | TPO (POE) | RTP |
| TES J-1200/10/V0/ND WT | Techmer Engineered Solutions | ABS | TES |
| Baydur® 660 IBS (25 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| CYCOLAC™ X11 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| Kepital® F20-03 BBK | KEP Americas | Acetal (POM) Copolymer | Kepital® |