Description: H 216 is a high melt flow rate homopolymer with narrow molecular weight distribution, designed for high thoughness fibers process. H 216 exhibits excellent processability with good melt stability and toughness/impact balance. Applications: Staple fibers and continuous filaments with high toughness and low denier; Fibers for reinforcement of asbestos-free concrete and roof tiles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, Injection Molded | 103 | ASTM D785 | |
| R-Scale | 103 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 36.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Yield, Injection Molded) | 9.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 1% Secant : Injection Molded | 1450 | MPa | ASTM D790 |
| Injection Molded | 1500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, Injection Molded | 25 | J/m | ASTM D256 |
| 23°C, Injection Molded | 1.9 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, Injection Molded | 103 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 103 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, Injection Molded | 59.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 59.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 151 | °C | ISO 306/A, ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO S2035 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| LNP™ THERMOCOMP™ DX09402 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| PEARLSTICK® 45-90/03 | Lubrizol Advanced Materials, Inc. | TPU-Capro | PEARLSTICK® |
| Plenco 05118 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |
| POLYCOMPO PP E111G | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |