Badamid® UL A703 GF25 FR HF is a Polyamide 66 (Nylon 66) material filled with 25% glass fiber. It is available in Europe for injection molding. Important attributes of Badamid® UL A703 GF25 FR HF are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.41 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 2.2 | -- | % | |
| Equilibrium, 23°C, 50% RH | 6.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8800 | 6000 | MPa | ISO 527-2/1 |
| Tensile Stress 1(Break, 23°C) | 115 | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain 2(Break, 23°C) | 2.5 | 3.5 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | |||
| -30°C | 6.0 | -- | kJ/m² | |
| 23°C | 7.0 | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | |||
| -30°C | 47 | -- | kJ/m² | |
| 23°C | 55 | 65 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 5 | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 245 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 6 | 262 | -- | °C | ISO 3146 |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 130 | -- | °C | |
| some hours | 240 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 7 | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity 8 | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Electric Strength 9 | 45 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity 10(1 MHz) | 3.50 | 4.60 | IEC 60250 | |
| Dissipation Factor 11(1 MHz) | 0.017 | 0.10 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.400 mm 12 | V-0 | -- | ||
| 0.800 mm 13 | V-0 | -- | ||
| Glow Wire Flammability Index (0.400 to 3.00 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.50 mm) | 775 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | 80x10x4 mm |
| 4 . | 80x10x4 mm |
| 5 . | 110x10x4 mm |
| 6 . | 10 K/min, Compound for moulding |
| 7 . | 80x80x1 mm |
| 8 . | 80x80x1 mm |
| 9 . | 80x80x1 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 125x13x0.8 mm |
| 13 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SF401 | RJM International, Inc. | PPE | RJM |
| Sinvicomp SFW7500 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Geon™ Vinyl Flexible D9501 NATURAL | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| SQUARE® SCR2510-20A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |
| NORYL PPX™ PPX7110 resin | SABIC Innovative Plastics | PPE+PS+PP | NORYL PPX™ |