Minlon® 73M30 NC010
| Category: | Nylon 6 , MINERAL REINFORCED NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Minlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZL4DV8_Minlon-73M30-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Mineral Reinforced Polyamide 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.90 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 6.3 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.1 | -- | % | |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4800 | 1700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 82.0 | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 | 40 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 1180 | MPa | |
| 1000 hr | -- | 740 | MPa | |
| Flexural Modulus | 4800 | 1800 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.5 | 3.5 | kJ/m² | |
| 23°C | 5.5 | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 85 | 85 | kJ/m² | |
| 23°C | 110 kJ/m² | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 5.5 | 9.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 196 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 78.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | -- | °C | ISO 306/B50 |
| Melting Temperature 1 | 221 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 8.8E-5 | -- | cm/cm/°C | |
| Transverse | 1.0E-4 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification (0.850 mm) | HB | -- | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® VEP15C | BASF Leuna GmbH | Nylon 6 | Miramid® |
| XYRON™ L554V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| NOVALAC RX®431 | Vyncolit N.V. | Phenolic | NOVALAC |
| Karina BLACK PVC COMPOUND -E MCP 520 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Mitsui EPT™ 4045M | Mitsui Chemicals, Inc. | EPDM | Mitsui EPT™ |