Stat-Rite® S408
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Stat-Rite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZKpIOe_Stat-Rite-S408.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stat-Rite® S408 is a static dissipative olefin copolymer alloy. Stat-Rite® S408 utilizes the patented Stat-Rite® inherently dissipative polymer (IDP) alloy system to provide clean, permanent ESD protection. Stat-Rite® IDP alloys provide consistent static dissipation even when extruded, injection molded or thermoformed into components. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 76 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1960 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 45.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 1860 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 80 | J/m | ASTM D256 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- 1 | 7.0E+9 | ohms | ESD S11.11 |
| -- 2 | 7.0E+10 | ohms | ASTM D257 |
| Volume Resistivity | 9.0E+10 | ohms·cm | ESD S11.12 |
| Static Decay 3 | |||
| +1000 V to 10 V | < 15.0 | sec | |
| +1000 V to 100 V | < 8.0 | sec | |
| Tribocharge - Nitrile Glove | < 30.0 | V | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ionic Content | Internal Method | ||
| Anions Cl- | 20.0 | ng/cm² | |
| Anions NO3- | 35.0 | ng/cm² | |
| Anions PO4- | < 50.0 | ng/cm² | |
| Anions SO4- | < 40.0 | ng/cm² | |
| Cations Ca | 25.0 | ng/cm² | |
| Cations K | 2.00 | ng/cm² | |
| Cations Li | < 60.0 | ng/cm² | |
| Cations Mg | < 3.00 | ng/cm² | |
| Cations Na | < 20.0 | ng/cm² | |
| Cations NH4 | < 3.00 | ng/cm² | |
| Outgassing | Internal Method | ||
| MMA | < 0.0300 | µg/g | |
| Styrene | < 0.0200 | µg/g | |
| Toluene | < 0.0200 | µg/g | |
| Total Organics | < 1.00 | µg/g |
| Note Message | |
|---|---|
| 1 . | 12% RH |
| 2 . | 50% RH |
| 3 . | CPM, 12% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Butyrate 565A3720023 Clear, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| Mylar® WC (500 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| TECACOMP® PEEK 450 PVX black 9585 | Ensinger GmbH | PEEK | TECACOMP® |
| LNP™ VERTON™ MV006SU compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |
| Durethan® DP 2801 000000 | LANXESS Corporation | Nylon 66 | Durethan® |