AT 472
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | AT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZKaIQM_AT-472.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This multi-purpose resin provides superior performance in low speed, low neck-in extrusion coating applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.917 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.6 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 94 | ||
| Shore D | 50 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 11.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 550 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 230 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 86.0 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 290 to 330 | °C | |
| Maximum Line Speed | 3.6 | m/sec | |
| Minimum Coating Thickness 3 | 10 | µm |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | 6 lb/ream |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A RELY 5922R 10000 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| Vistek 1963 F | Visual Polymer Technologies, LLC | TP, Unspecified | Vistek |
| TIPPLEN® H 145 F | MOL Petrochemicals Co. Ltd. | PP Homopolymer | TIPPLEN® |
| ALTECH® PC C 1000/149 FR | ALBIS PLASTIC GmbH | PC | ALTECH® PC |
| Lupox® GP2056F | LG Chem Ltd. | PBT | Lupox® |