Category: | Nylon 66 , Polyamide 66 |
Manufacturer: | Tyne Plastics LLC. |
Trademark: | TYLON® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | ZKZy9G_TYLON-1433.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Data was measured on natural colored test specimens. |
General Information | |
---|---|
Filler / Reinforcement |
|
Forms |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
Molding Shrinkage - Flow (3.18 mm) | 0.20 to 0.40 | % | ASTM D955 |
Water Absorption (24 hr) | 0.70 | % | ASTM D570 |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Rockwell Hardness (M-Scale) | 101 | ASTM D785 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength | 165 | MPa | ASTM D638 |
Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
Flexural Modulus | 9650 | MPa | ASTM D790 |
Flexural Strength | 248 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (6.35 mm) | 80 | J/m | ASTM D256 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load | ASTM D648 | ||
0.45 MPa, Unannealed | 257 | °C | |
1.8 MPa, Unannealed | 249 | °C |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
TOTAL Polyethylene HDPE XS 10 OS | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
ALAMID® 6.6 GF 30 MOD WL SCHWARZ-9665 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | ALAMID® |
Diofan® A 063 | Solvay Specialty Polymers | PVDC | Diofan® |
Ghaed ABS ABS-HU-650 | Ghaed Basir Petrochemicals Co. | ABS | Ghaed ABS |
Plexiglas® Diffuse™ V045-68207 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |