Braskem PP CP 442 XP
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Braskem |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZKGg5l_Braskem-PP-CP-442-XP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: CP 442XP is a medium melt flow rate heterophasic copolymer suitable for injection moulding applications. The product combines good stiffness with excellent impact resistance even at sub-zero temperatures and also provides good surface properties and excellent processability. Applications: Automotive parts; Battery cases; Toys; Household Appliances; Crates; Buckets; Compounds. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.895 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, Injection Molded | 68 | ASTM D785 | |
| R-Scale | 68 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 24.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Yield, Injection Molded) | 7.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 1% Secant : Injection Molded | 1100 | MPa | ASTM D790 |
| Injection Molded | 1050 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -20°C, Injection Molded | 50 | J/m | ASTM D256 |
| 23°C, Injection Molded | No Break | ASTM D256 | |
| -20°C, Injection Molded | 4.4 | kJ/m² | ISO 180 |
| 23°C, Injection Molded | 34 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, Injection Molded | 93.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 93.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, Injection Molded | 52.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 52.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/A, ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax PL338 | INDELPRO, S.A. de C.V. | PP Homopolymer | Pro-fax |
| Cellophane™ 350P00 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Kareline® PPMS5050 EC | Plasthill Oy | PP Homopolymer | Kareline® |
| LG ABS BM662B | LG Chem Ltd. | ABS | LG ABS |
| POCAN® BFN 4231 000000 | LANXESS GmbH | PBT | POCAN® |