ACLAM® TC100 (6 mil)
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Honeywell |
| Trademark: | ACLAM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZIIgbz_ACLAM-TC100-6-mil-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aclam® TC100 is a low temperature heat sealable lamination composed of a 2 mil (50µ) polyolefin heat seal layer and a 4 mil (100µ) proprietary Aclar® 11C film layer. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With Metal-Dynamic | 0.43 | ASTM D1894 | |
| With metal-static | 0.55 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD : 51 µm | 1000 | MPa | ASTM D882 |
| TD : 51 µm | 965 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 38.6 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 27.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 51 µm | 230 | % | ASTM D882 |
| TD : Yield, 51 µm | 150 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 500 | g | ASTM D1922 |
| TD : 51 µm | 1600 | g | ASTM D1922 |
| Oxygen Permeability (23°C, 51 µm, 0% RH) | 0.79 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate | ASTM F1249 | ||
| 50°C, 90% RH | 0.26 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 38°C, 100% RH | 0.062 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Additional Information |
|---|
| Yield, No Standard: 3.84 m²/kgUnderwriter's Laboratory, UL 94: VTM-1Coef of Friction, ASTM D1894, vs Metal - Dynamic: 0.4 to 0.45Coef of Friction, ASTM D1894, vs Metal - Static: 0.5 to 0.6 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ CP0437W10L1 | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Gallonprene® GP520-5004 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Epoxies, Ect. 60-7156 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| MAXATEL® AC90TFSi-BK | Pier One Polymers, Inc. | Acetal (POM) Copolymer | MAXATEL® |
| Starex TX-0550 | LOTTE ADVANCED MATERIALS CO., LTD. | MABS | Starex |