BJB Polyurethane WC-775 A/B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZGqRQt_BJB-Polyurethane-WC-775-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WC-775 A/B produces a high impact rigid 75 Shore D material that is commonly used to make clear or tinted castings of all kinds. When used at room temperature, castings 1/8" thick or larger can be readily cast. Castings that are less than 1/8" thick will generally require a mild post-cure. This product may exhibit a slight yellowing or color change when exposed to direct UV light. PRODUCT HIGHLIGHTS:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 1.03 | g/cm³ | |
| -- 2 | 1.08 | g/cm³ | |
| -- | 1.09 | g/cm³ | |
| Specific Volume | 0.961 | cm³/g |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Gel Time | 20.0 | min | |
| Work Time (25°C) 3 | 15.0 | min |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Brookfield Viscosity | |||
| Mixed : 25°C | 600 to 700 | mPa·s | |
| Part A : 25°C | 650 | mPa·s | |
| Part B : 25°C | 400 | mPa·s |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.50 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 76 to 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1860 | MPa | ASTM D638 |
| Tensile Strength | 47.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 62 | % | ASTM D638 |
| Flexural Modulus | 1450 | MPa | ASTM D790 |
| Flexural Strength | 54.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 62 | J/m | ASTM D256 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 95, Mix Ratio by Volume: 91 | ||
| Part B | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Demold Time (25°C) | 960 to 1400 | min | |
| Post Cure Time (25°C) | 120 to 170 | hr |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | 100g mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Milastomer™ S-650BS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| Tekulac ST 18 | TEKUMA Kunststoff GmbH | ABS | Tekulac |
| Sup-tech P620 | Shanghai Suptech Engineering Plastics Co. Ltd. | PP, Unspecified | Sup-tech |
| Yuyao PPO GFN1726 | Yuyao Tenglong Plastics Co., Ltd. | PPE+PS | Yuyao PPO |
| Arnite® A06 700 | DSM Engineering Plastics | PET | Arnite® |