Elastollan® WY1157
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | BASF Corp. Thermoplastic Polyurethanes |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZGPUU3_Elastollan-WY1157.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Elastollan® WY1157 exhibits excellent toughness, high and low temperature properties, hydrolytic stability and burst pressures for hose and tube applications. Elastollan® WY1157 is supplied uncolored in pellet form. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 54 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 124 | MPa | ASTM D412 |
| Flexural Modulus (Injection Molded) | 152 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 150 | mg | ASTM D1044 |
| Abrasion - DIN | 80 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Point - DMA | 107 | °C | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 22.8 | MPa | |
| 300% Strain | 28.3 | MPa | |
| Tensile Strength | 34.5 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 440 | % | ASTM D412 |
| Tear Strength 1 | 161 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 20 | % | |
| 70°C, 22 hr | 55 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -33.0 | °C | Internal Method |
| Vicat Softening Temperature | 135 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 210 to 230 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 210 to 230 | °C | |
| Nozzle Temperature | 220 to 240 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax PF531 | LyondellBasell Industries | PP Homopolymer | Pro-fax |
| Caltex PP MU42 | GS Caltex | PP, Unspecified | Caltex PP |
| Axiall PVC SP-7008 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| POLYFLON™ M-15HS | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |
| ADENE® N09CTE-00 | A.D. Compound S.p.A. | PP Homopolymer | ADENE® |