LNP™ LUBRICOMP™ WFL36 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZFH6v9_LNPLUBRICOMPWFL36compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP WFL36 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE. Also known as: LNP* LUBRICOMP* Compound WFL-4036 Product reorder name: WFL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 13.0 - 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.20 - 0.40 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.080 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 112 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.9 | % | ISO 527-2/5 |
| Flexural Modulus 2 | ISO 178 | ||
| -- | 8900 | MPa | ISO 178 |
| 60°C | 5800 | MPa | ISO 178 |
| 100°C | 4700 | MPa | ISO 178 |
| 150°C | 3600 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 200 | MPa | ISO 178 |
| 60°C | 127 | MPa | ISO 178 |
| 100°C | 103 | MPa | ISO 178 |
| 150°C | 75.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.57 | ASTM D3702 Modified | |
| With Self-Static | 0.41 | ASTM D3702 Modified | |
| Flexural Strain at Break 3 | ISO 178 | ||
| -- | 3.1 | % | ISO 178 |
| 60°C | 4.6 | % | ISO 178 |
| 100°C | 5.1 | % | ISO 178 |
| 150°C | 5.5 | % | ISO 178 |
| Wear Factor - Washer | 42.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -40°C 4 | 9.0 | kJ/m² | ISO 180/1A |
| 23°C 5 | 9.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6 | ISO 180/1U | ||
| -40°C | 60 | kJ/m² | ISO 180/1U |
| 23°C | 50 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, unannealed, 64.0mm span | 222 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 207 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 8.4E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1750 | J/kg/°C | ASTM E1269 |
| Thermal Conductivity | 0.26 | W/m/K | ASTM D5930 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 - 232 | °C | |
| Middle Temperature | 243 - 254 | °C | |
| Front Temperature | 260 - 271 | °C | |
| Processing (Melt) Temp | 238 - 266 | °C | |
| Mold Temperature | 82.2 - 98.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 80*10*3 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teflon® PTFE 601A | DuPont Fluoropolymers | PTFE | Teflon® PTFE |
| SLOVAMID® 6 GF 30 HTS | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Anjacom® 200C-P | Almaak International GmbH | Nylon 6 | Anjacom® |
| Grilamid® L 25 NZ ESD | EMS-GRIVORY | Nylon 12 | Grilamid® |
| Hydrin® T5010 | Zeon Chemicals L.P. | Epoxy | Hydrin® |