Daicel PP PNAK2
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Daicel PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZFGRvs_Daicel-PP-PNAK2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Daicel PP PNAK2 is a Polypropylene material. It is available in Asia Pacific. Primary attribute of Daicel PP PNAK2: Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.5 to 1.8 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 97 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2 |
| Flexural Modulus | 1900 | MPa | ISO 178 |
| Flexural Stress | 48.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 140 to 180 | °C | |
| Middle Temperature | 160 to 200 | °C | |
| Front Temperature | 180 to 220 | °C | |
| Nozzle Temperature | 180 to 220 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 5.00 to 20.0 | MPa | |
| Screw Speed | 70 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 246M NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| SUMIKAEXCEL® PES 4100G | Sumitomo Chemical Co., Ltd. | PESU | SUMIKAEXCEL® PES |
| ALCOM® PA66 910/1.1 CF15 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| IROSTIC® S 8735 | Huntsman Corporation | TPU, Unspecified | IROSTIC® |
| Moplen EP6051 | LyondellBasell Industries | PP, Unspecified | Moplen |