KumhoSunny PBT/PET HEB4050M
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PBT/PET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZF12Ss_KumhoSunny-PBT-PET-HEB4050M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEB4050M is a mineral filled PBT/PET alloy resin, offering good mechanical properties, outstanding appearance, very low haze and excellent processing properties. HEB4050M is recommended for headlight lamp,such as bezel,etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.45 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 1.2 to 1.5 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 45.0 | MPa | ISO 527-2/5 |
| Flexural Modulus 1 | 3600 | MPa | ISO 178 |
| Flexural Stress 2 | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 3.5 | kJ/m² | |
| 23°C | 5.5 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(0.45 MPa, Unannealed) | 200 | °C | ISO 75-2/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 250 to 255 | °C | |
| Nozzle Temperature | 255 to 265 | °C | |
| Processing (Melt) Temp | 245 to 265 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Back Pressure | 0.200 to 0.800 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® SJ6300C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| CP PRYME® Nylon 6 N233HSL | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |
| KEBAFLEX® E D 50.1 | BARLOG plastics GmbH | TPV | KEBAFLEX® |
| Petrotene® PP A3 C40 NTLA010 PH309 | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |
| Telcar® TL-88-N873F | Teknor Apex Company | TPE | Telcar® |