Baydur® TB 100-15 Thermal Break System
| Category: | PUR-MDI , Polyurethane (MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baydur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZEhHfM_Baydur-TB-100-15-Thermal-Break-System.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The Baydur TB 100-15 thermal break system produces a structural, full density polyurethane used for window applications. The system is supplied as two reactive liquid components. Component A is a polymeric diphenylmethane diisocyanate (PMDI), and Component B is a formulated polyol system that is phase stable. Baydur TB 100-15 is a fast debridging system, designed to have excellent physical properties while exhibiting minimal wet shrinkage. As with any product, use of the Baydur TB 100-15 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D1622 |
| K (wear) Factor | 0.13 | W/m/K | ASTM C518 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shaw D, 5 seconds, 6.35mm) | 78 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 6.35 mm) | 39.3 | MPa | ASTM D638 |
| Tensile Elongation (Break, 6.35 mm) | 30 | % | ASTM D638 |
| Flexural Modulus (6.35 mm) | 1550 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.35 mm) | 81.1 | °C | ASTM D648 |
| Thermoset | Nominal Value | ||
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 85, mixing ratio by capacity: 75 | ||
| Component B | Mixing ratio by weight: 100, mixing ratio by capacity: 100 |
| Additional Information |
|---|
| Part A Type: Isocyanate Appearance: Dark brown liquid Specific Gravity @ 25°C: 1.24 Viscosity @25°C: 200 cps Weight per Gallon: 10.35 lbs Part B Type: Polyol Appearance: Black liquid Specific Gravity @ 25°C: 1.08 Viscosity @25°C: 600 cps Weight per Gallon: 9.01 lbs Processing Conditions Material Temperature: 70 to 95°F Hand Mix Reactivity, 80°F: 20 sec Machine Reactivity, 80°F: 12 to 15 sec Debridge Time: 5 to 10 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE B5421 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Elastane™ 4725-85A | Technical Polymers, LLC | TPU-Polyester | Elastane™ |
| Sylvin 802-94 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ VERTON™ RV00AE compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |
| LEXAN™ 123X resin | SABIC Innovative Plastics | PC | LEXAN™ |