BJB Epoxy TC-1604 A/B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Epoxy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZEbv9h_BJB-Epoxy-TC-1604-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
TC-1604 A/B is a filled, easy to apply, laminating epoxy resin for variety of fabricating applications.Designed to be used with heavier weight fiberglass cloth (typically 8-10 oz. tooling fabric), TC-1604 can produce thick laminates without excess draining of the resin. Being a very stable system with low shrinkage, its common usages include:
It features the ability to cure at room temperature for applications that do not require a working service temperature above 224°F (107°C). TC-1604 can also be used as an adhesive for bonding wood, composites, and other materials. Adding fillers like fumed silica, micro-spheres, and short-strand fibers can create pastes for fillets, fairings, and bonding applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Specific Gravity | |||
| Part A : 25°C | 1.280 | g/cm³ | |
| Part B : 25°C | 1.017 | g/cm³ | |
| Water Absorption - 100 hr | 1.3 | % | ASTM D570 |
| Shrinkage | 0.015 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Work Time (25°C) 1 | 20.0 | min |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Brookfield Viscosity - Mixed (25°C) | 8.00 | Pa·s |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 89 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 221 | MPa | ASTM D638 |
| Flexural Modulus | 15900 | MPa | ASTM D790 |
| Flexural Strength | 269 | MPa | ASTM D790 |
| Compressive Strength | 276 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 107 | °C | ASTM D648 |
| CLTE - Flow | 2.2E-5 | cm/cm/°C | ASTM D3386 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 12 | ||
| Shelf Life | 52 | wk |
| Note Message | |
|---|---|
| 1 . | 1 lb mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ H12LW | Mando Advanced Materials Co., Ltd. | ABS+Nylon | TEKAMID™ |
| Viprene™ G80A-32U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| Karina WHITE PVC COMPOUD -E 811-10/184-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plenco 04485 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |
| Sylvin 9600-100UV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |