PALSAFE® R 05 GF 20

Category:	PC , Polycarbonate
Manufacturer:	pal plast GmbH
Trademark:	PALSAFE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ZEU0N5_PALSAFE-R-05-GF-20.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
PALSAFE®R 05 GF 20 is a polycarbonate (PC) product, which contains a 20% glass fiber reinforced material. It can be processed by injection molding and is available in Europe. Typical application areas are: electrical/electronic applications. Features include: flame retardant/rated flame high viscosity

General Information
Filler / Reinforcement	Glass fiber reinforced material, 20% filler by weight
Features	Viscosity, High
Uses	Electrical/Electronic Applications
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.34	g/cm³	ISO 1183
Water Absorption			ISO 62
Saturated, 23°C	0.28	%	ISO 62
Equilibrium, 23°C, 50% RH	0.14	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	5500	MPa	ISO 527-2/1A/1
Tensile Stress (Break, 23°C)	100	MPa	ISO 527-2/1A/5
Tensile Strain (Break, 23°C)	3.5	%	ISO 527-2/1A/5

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	148	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	175	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	V-2 V-1		UL 94

Additional Information
Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 5000 to 6000 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 95 to 105 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 3 to 4 %Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 146 to 149 °CDensity, ISO 1183: 1.33 to 1.35 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.25 to 0.3 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.12 to 0.15 %

Additional Information

Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 5000 to 6000 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 95 to 105 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 3 to 4 %Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 146 to 149 °CDensity, ISO 1183: 1.33 to 1.35 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.25 to 0.3 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.12 to 0.15 %

Resin Grade	Manufacturer	Category	Trademark
NEXT REGRIND PA6 8233-300RG	NEXT Specialty Resins, Inc.	Nylon 6	NEXT REGRIND
Network Polymers HDPE 50 5502	Network Polymers, Inc.	HDPE	Network Polymers HDPE
Allen ABS 552/LXS	SEKISUI Polymer Innovations, LLC	ABS	Allen ABS
Grivory® GVL-4H nat	EMS-GRIVORY	Nylon 66+Nylon 6I/X	Grivory®
Karina GRAY COLOR CONCENTRATE 18/367-FC-LMP	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina