SEPAZ™ C140GM
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | SEPAZ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZDtYXs_SEPAZ-C140GM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SEPAZ™ C140GM is a Liquid Crystal Polymer (LCP) product filled with 40% glass\mineral. It is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.73 | g/cm³ | ASTM D792 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow | 0.10 | % | |
| Across Flow | 0.40 | % | |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 112 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 13200 | MPa | ASTM D790 |
| Flexural Strength | 164 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 6.9 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 269 | °C | ASTM D648 |
| Peak Melting Temperature | 335 | °C | ASTM D2133 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Constant | 3.60 | ASTM D150 | |
| Dissipation Factor | 0.023 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 350 to 360 | °C | |
| Mold Temperature | 40.0 to 150 | °C |
| Note Message | |
|---|---|
| 1 . | 60°C Mold Temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 121-65M300 | ExxonMobil Chemical | TPV | Santoprene™ |
| DOMAMID® A1-025-B30-N | DOMO Engineering Plastics GmbH | Nylon 6 | DOMAMID® |
| Elastron® G G500.A23.B.PA | Elastron USA, Inc. | SEBS | Elastron® G |
| Huafon HF-1195A | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| LNP™ LUBRICOMP™ EX07305 compound | SABIC Innovative Plastics Asia Pacific | PEI | LNP™ LUBRICOMP™ |